【概要描述】In the production of welded pipes with high frequency welded pipe equipment, the manifestations of cracks include long cracks, partial periodic cracks, and irregular intermittent cracks. Some steel pipes have no cracks on the surface after welding, but cracks appear after flattening, straightening or water pressure tests.

Prevention of pipe making weld cracking of high frequency welded pipe equipment (1)

【概要描述】In the production of welded pipes with high frequency welded pipe equipment, the manifestations of cracks include long cracks, partial periodic cracks, and irregular intermittent cracks. Some steel pipes have no cracks on the surface after welding, but cracks appear after flattening, straightening or water pressure tests.

  • Sort:Information
  • Auth:
  • Source:
  • Release time:2023-08-28 11:30
  • Pvs:
Detail

In the production of welded pipes with high frequency welded pipe equipment, the manifestations of cracks include long cracks, partial periodic cracks, and irregular intermittent cracks. Some steel pipes have no cracks on the surface after welding, but cracks appear after flattening, straightening or water pressure tests.

 

High frequency welded pipe equipment

 

There are three main reasons that affect the cracks in the production of high frequency welded pipe equipment: ①The quality of raw materials is poor. ②Edge joint state. ③The selection of process parameters is unreasonable. We explain and prevent the influencing factors of poor quality of raw materials and the state of edge joints.

 

① Poor quality of raw materials

In the production of welded pipes, large edge burrs and excessive width of the raw material are often problems.

If the burr is outwards during welding, it is easy to produce continuous and long intermittent cracks;

The width of the raw material is too wide, and the squeeze roll pass is over-filled, forming a welded peach shape, with large outer weld scars, small or no inner weld ribs, and cracks after straightening.

 

②Edge joint state

The fillet joint state of the edge of the tube blank is a common phenomenon in the production of welded pipes. The smaller the pipe diameter, the more serious the fillet joint.

Inadequate forming adjustment is a prerequisite for corner joints.

The improper design of the squeeze roller pass, the large outer corner of the pass, and the elevation angle of the squeeze roller adjustment are the key factors that affect the corner joint.

 

The single-radius squeeze roll pass cannot eliminate the corner joint problems caused by poor forming. Increase the squeezing force, or the squeeze roll pass wears in the later stage of production and becomes a vertical oval, which intensifies the sharp peach-shaped welding state. Severe corner joints occur.

The corner joint will cause most of the metal to flow out from the upper side, forming an unstable melting process. At this time, there will be large metal splashes, overheated weld joints, and external burrs that are hot, irregular, large and not easy to scratch If the welding speed is slightly improperly controlled, the "false welding" of the weld will inevitably occur.

 

High frequency welded pipe equipment

 

The outer corner of the squeeze roller is large, which makes the tube blank insufficiently filled in the squeeze roller, and the edge contact state changes from parallel to a "V" shape, and there is a phenomenon that the inner weld is not welded.

 

The squeeze roller shaft is stressed and worn for a long time, and the base bearing is worn, and the two shafts form an elevation angle, resulting in insufficient squeezing force, vertical ellipse and serious angle joint.

 

The factors that affect the production of longitudinal welded pipes with high frequency welded pipe equipment are to be prevented according to the actual situation to prevent weld cracks during the production of longitudinal welded pipes.

关键词:

More News

Factors and various influences to ensure the quality of used high frequency welded pipe machine welded pipe products(1)
Factors and various influences to ensure the quality of used high frequency welded pipe machine welded pipe products(1)
In the process of producing welded pipes with used high frequency welded pipe machine, how to ensure that the product quality meets the requirements of technical standards and the needs of customers, it is necessary to analyze the factors affecting product quality in the production process of steel pipes.
Detail
In the process of producing welded pipes with used high frequency welded pipe machine, how to ensure that the product quality meets the requirements of technical standards and the needs of customers, it is necessary to analyze the factors affecting product quality in the production process of steel pipes.
Improving lubricating effect of flying saw on used welded pipe equipment
Improving lubricating effect of flying saw on used welded pipe equipment
Through the technical improvement of the used welded pipe equipment, the lubrication of the gear and rack of the flying saw has been effectively improved, and the specific performance is as follows:
Detail
Through the technical improvement of the used welded pipe equipment, the lubrication of the gear and rack of the flying saw has been effectively improved, and the specific performance is as follows:
Why does the used roll forming machine flying saw saw lack of lubrication?
Why does the used roll forming machine flying saw saw lack of lubrication?
When the used roll forming machine produces steel pipes, the pipe fittings move at a constant speed according to the set speed, and the saw car is stationary relative to the unit before the sawing process. When the steel pipe reaches the set length, the clamping device of the saw car clamps the steel pipe, and the drive mechanism drives the saw car to move with the steel pipe and perform the sawing process until the sawing operation is completed. When the sawing process of the flying saw is completed, the driving device drives the saw carriage to return to the initial position. The reciprocating motion of the saw car is realized by the relative movement of the rack at the bottom of the saw car and the gear fixedly installed on the machine bed system.
Detail
When the used roll forming machine produces steel pipes, the pipe fittings move at a constant speed according to the set speed, and the saw car is stationary relative to the unit before the sawing process. When the steel pipe reaches the set length, the clamping device of the saw car clamps the steel pipe, and the drive mechanism drives the saw car to move with the steel pipe and perform the sawing process until the sawing operation is completed. When the sawing process of the flying saw is completed, the driving device drives the saw carriage to return to the initial position. The reciprocating motion of the saw car is realized by the relative movement of the rack at the bottom of the saw car and the gear fixedly installed on the machine bed system.
Weld quality failure caused by used welded pipe machines (9)
Weld quality failure caused by used welded pipe machines (9)
When manufacturing welded pipes for used welded pipe machines, judging that the quality of the welded pipes meets the standard depends on the quality of the welds. Therefore, the quality of the weld is very important, so sometimes it is necessary to rule out the quality of the weld. We perform analyses to understand weld quality failures.
Detail
When manufacturing welded pipes for used welded pipe machines, judging that the quality of the welded pipes meets the standard depends on the quality of the welds. Therefore, the quality of the weld is very important, so sometimes it is necessary to rule out the quality of the weld. We perform analyses to understand weld quality failures.
Contact information
Tel: +86-13392281699
Wechat: 13392281699
Email: zty@usedpipemill.com
Company address:No. A99, East Lecong Avenue, Lecong Town, Foshan City, Guangdong Province

Recommendation

Online Inquiry

留言应用名称:
底部留言
描述:

LINK

Contact Us

Tel (wechat): 13336487288
Wechat:+86 13336487288

WhatsApp:+86 13336487288
Email: zty@usedpipemill.com

Address: No. A99, Lecong Avenue East, Lecong Town, Foshan City, Guangdong Province

QRCODE

Copyright 0 2021 jinyujie. 粤ICP备13051810号 Powerby:  300.cn