【概要描述】There may be various defects in the used high frequency welded pipe equipment, and the names of defects are not completely uniform. Combined with the characteristics of our welded pipe production, the defects that often occur are as follows:①Inclusions; ②Insufficient fusion; ③Stick welding; ④Cast welding;Not all of these defects are present, but they are often found in high-frequency welded pipes.

Common welding defects of used high frequency welded pipe equipment (3)

【概要描述】There may be various defects in the used high frequency welded pipe equipment, and the names of defects are not completely uniform. Combined with the characteristics of our welded pipe production, the defects that often occur are as follows:①Inclusions; ②Insufficient fusion; ③Stick welding; ④Cast welding;Not all of these defects are present, but they are often found in high-frequency welded pipes.

  • Sort:Information
  • Auth:
  • Source:
  • Release time:2023-03-03 11:30
  • Pvs:
Detail

There may be various defects in the used high frequency welded pipe equipment, and the names of defects are not completely uniform. Combined with the characteristics of our welded pipe production, the defects that often occur are as follows:

①Inclusions; ②Insufficient fusion; ③Stick welding; ④Cast welding;

Not all of these defects are present, but they are often found in high-frequency welded pipes.

 

The schematic diagrams provided below are not actual pictures of each defect, and are mainly used to illustrate the main characteristics of the defect, and do not mistakenly believe that welding defects are only produced under a specific process condition. The defect shown in the text is the fracture morphology of the weld cracked by the flattening test.

 

Other common welding defects of used high frequency welded pipe equipment can be divided into ① casting welding (brittle welding); ② porosity (pinhole); ③ jump welding.

 

Cast welding (brittle welding)

Casting welding means that the molten metal on the joint surface is not fully discharged, and the as-cast metal on the fusion surface contains metal oxides like peroxidation, and the fracture morphology changes according to the residual as-cast metal content. Now most of them show flat and brittle morphology, and metallographic inspection can see that there is as-cast metal on the joint surface, as shown in Figure 11. The cast welded pipe cracks when it is flattened.

 

Used high frequency welded pipe equipment

 

Preventive measures for casting welding:

①Increase welding discharge;

②Increase the width of the steel strip.

 

Air holes (pinholes)

The pores on the welding joint surface of the used high frequency welded pipe equipment are caused by high temperature welding but insufficient discharge. The fracture morphology is fibrous, and the spherical bright white dots are randomly distributed on the entire fracture. When the white dots appear on the outer wall, the surface phenomenon of the white dots turns black due to oxidation. As shown in Figure 12.

 

Used high frequency welded pipe equipment

 

Small pores can be seen before the outer burr is removed, and pores can also be seen on the fusion line after the outer burr is removed.

 

Preventive measures for stomata:

①Reduce welding input;

②Increase the amount of extrusion.

 

Jump welding

There are various forms of jump welding, as shown in Figure 13.

 

Used high frequency welded pipe equipment

 

Usually, such defects are distributed regularly and continuously, and the defects outside the wall thickness are similar to wavy defects, and the spacing is generally equidistant.

 

Precautions for jump welding:

① Filter equipment to increase welding current;

② Check the input voltage;

③ Check the rollers and shafts.

 

Part of the content of this site comes from the Internet. This site only provides information storage. The copyright belongs to the original author. It does not bear the relevant legal responsibility and does not represent the views and positions of this site. Please contact and delete it if there is any infringement.

关键词:

More News

Factors and various influences to ensure the quality of used high frequency welded pipe machine welded pipe products(1)
Factors and various influences to ensure the quality of used high frequency welded pipe machine welded pipe products(1)
In the process of producing welded pipes with used high frequency welded pipe machine, how to ensure that the product quality meets the requirements of technical standards and the needs of customers, it is necessary to analyze the factors affecting product quality in the production process of steel pipes.
Detail
In the process of producing welded pipes with used high frequency welded pipe machine, how to ensure that the product quality meets the requirements of technical standards and the needs of customers, it is necessary to analyze the factors affecting product quality in the production process of steel pipes.
Improving lubricating effect of flying saw on used welded pipe equipment
Improving lubricating effect of flying saw on used welded pipe equipment
Through the technical improvement of the used welded pipe equipment, the lubrication of the gear and rack of the flying saw has been effectively improved, and the specific performance is as follows:
Detail
Through the technical improvement of the used welded pipe equipment, the lubrication of the gear and rack of the flying saw has been effectively improved, and the specific performance is as follows:
Why does the used roll forming machine flying saw saw lack of lubrication?
Why does the used roll forming machine flying saw saw lack of lubrication?
When the used roll forming machine produces steel pipes, the pipe fittings move at a constant speed according to the set speed, and the saw car is stationary relative to the unit before the sawing process. When the steel pipe reaches the set length, the clamping device of the saw car clamps the steel pipe, and the drive mechanism drives the saw car to move with the steel pipe and perform the sawing process until the sawing operation is completed. When the sawing process of the flying saw is completed, the driving device drives the saw carriage to return to the initial position. The reciprocating motion of the saw car is realized by the relative movement of the rack at the bottom of the saw car and the gear fixedly installed on the machine bed system.
Detail
When the used roll forming machine produces steel pipes, the pipe fittings move at a constant speed according to the set speed, and the saw car is stationary relative to the unit before the sawing process. When the steel pipe reaches the set length, the clamping device of the saw car clamps the steel pipe, and the drive mechanism drives the saw car to move with the steel pipe and perform the sawing process until the sawing operation is completed. When the sawing process of the flying saw is completed, the driving device drives the saw carriage to return to the initial position. The reciprocating motion of the saw car is realized by the relative movement of the rack at the bottom of the saw car and the gear fixedly installed on the machine bed system.
Weld quality failure caused by used welded pipe machines (9)
Weld quality failure caused by used welded pipe machines (9)
When manufacturing welded pipes for used welded pipe machines, judging that the quality of the welded pipes meets the standard depends on the quality of the welds. Therefore, the quality of the weld is very important, so sometimes it is necessary to rule out the quality of the weld. We perform analyses to understand weld quality failures.
Detail
When manufacturing welded pipes for used welded pipe machines, judging that the quality of the welded pipes meets the standard depends on the quality of the welds. Therefore, the quality of the weld is very important, so sometimes it is necessary to rule out the quality of the weld. We perform analyses to understand weld quality failures.
Contact information
Tel: +86-13392281699
Wechat: 13392281699
Email: zty@usedpipemill.com
Company address:No. A99, East Lecong Avenue, Lecong Town, Foshan City, Guangdong Province

Recommendation

Online Inquiry

留言应用名称:
底部留言
描述:

LINK

Contact Us

Tel (wechat): 13336487288
Wechat:+86 13336487288

WhatsApp:+86 13336487288
Email: zty@usedpipemill.com

Address: No. A99, Lecong Avenue East, Lecong Town, Foshan City, Guangdong Province

QRCODE

Copyright 0 2021 jinyujie. 粤ICP备13051810号 Powerby:  300.cn