【概要描述】In the production of welded pipes with used high frequency tube mills, the manifestations of cracks include long cracks, partial periodic cracks, and irregular intermittent cracks. Some steel pipes have no cracks on the surface after welding, but cracks appear after flattening, straightening or water pressure tests.

Used high frequency tube mills to prevent pipe welding seam cracking (2)

【概要描述】In the production of welded pipes with used high frequency tube mills, the manifestations of cracks include long cracks, partial periodic cracks, and irregular intermittent cracks. Some steel pipes have no cracks on the surface after welding, but cracks appear after flattening, straightening or water pressure tests.

  • Sort:Information
  • Auth:
  • Source:
  • Release time:2022-01-19 11:30
  • Pvs:
Detail

In the production of welded pipes with used high frequency tube mills, the manifestations of cracks include long cracks, partial periodic cracks, and irregular intermittent cracks. Some steel pipes have no cracks on the surface after welding, but cracks appear after flattening, straightening or water pressure tests.

 

There are three main reasons that affect the cracks in the production of used high frequency tube mills: ①The quality of raw materials is poor. ②Edge joint state. ③The selection of process parameters is unreasonable. We explain and prevent the influencing factors of poor quality of raw materials and the state of edge joints.

 

Used high frequency tube mills

 

③ Unreasonable selection of process parameters

The process parameters of high-frequency welded pipe production include welding speed (unit speed), welding temperature (high-frequency power), welding current (high-frequency frequency), extrusion force (grinding tool design and material), opening angle (grinding tool design and material) , Induction coil position), inductor (coil material, winding direction, position), and the size and placement of the resistor.

 

(1) High-frequency (steady and continuous) power, welding speed, welding extrusion force and opening angle are the most important process parameters, which must be matched reasonably, otherwise the quality of the weld will be affected.

① If the speed is too high or too low, it will cause low-temperature welding impermeability and high-temperature overburning, and the weld will crack after being flattened.

 

② When the squeezing force is insufficient, the edge metal to be welded cannot be fully pressed together, and the residual impurities in the weld are not easily discharged, and the strength of the weld is reduced;

When the squeezing force is too large, the metal flow angle increases, the residue is easily discharged, the heat-affected zone becomes narrower, and the welding quality is improved. However, if the pressure is too high, it will cause large sparks and splashes, causing the molten oxide and part of the plastic layer of metal to be squeezed out, and the weld will be thinned after being scratched, thereby reducing the strength of the weld and cracking.

Proper extrusion force is an important prerequisite for weld quality.

 

③ If the opening angle is too large, the high-frequency proximity effect is reduced, the eddy current loss is increased, and the welding temperature is reduced. If welding at the original speed, cracks will occur;

If the opening angle is too small, the welding current will be unstable, and a small blast (intuitively a discharge phenomenon) will occur at the squeezing point and cracks will be formed.

 

Used high frequency tube mills

 

(2) The inductor (coil) is the main part of the welding part of the high-frequency welded pipe. The gap between it and the pipe blank and the width of the opening have a great influence on the quality of the weld.

① The gap between the inductor and the tube blank is too large, causing the efficiency of the inductor to drop sharply;

If the gap between the inductor and the tube blank is too small, it is easy to cause electric discharge between the inductor and the tube blank, causing weld cracks, and it is also easy to be damaged by the tube blank.

 

② The opening width of the sensor is too large, which reduces the welding temperature of the butt edge of the tube blank. In the case of a faster welding speed, it is easy to produce false welding, which will crack after straightening.

 

In the production of longitudinal welded pipes with used high frequency tube mills, there are many factors that cause weld cracks, and the prevention methods are also different. There are too many variables in the high-frequency welding process, and any link defect will ultimately affect the quality of the weld. The above are some common factors.

关键词:

More News

Factors and various influences to ensure the quality of used high frequency welded pipe machine welded pipe products(1)
Factors and various influences to ensure the quality of used high frequency welded pipe machine welded pipe products(1)
In the process of producing welded pipes with used high frequency welded pipe machine, how to ensure that the product quality meets the requirements of technical standards and the needs of customers, it is necessary to analyze the factors affecting product quality in the production process of steel pipes.
Detail
In the process of producing welded pipes with used high frequency welded pipe machine, how to ensure that the product quality meets the requirements of technical standards and the needs of customers, it is necessary to analyze the factors affecting product quality in the production process of steel pipes.
Improving lubricating effect of flying saw on used welded pipe equipment
Improving lubricating effect of flying saw on used welded pipe equipment
Through the technical improvement of the used welded pipe equipment, the lubrication of the gear and rack of the flying saw has been effectively improved, and the specific performance is as follows:
Detail
Through the technical improvement of the used welded pipe equipment, the lubrication of the gear and rack of the flying saw has been effectively improved, and the specific performance is as follows:
Why does the used roll forming machine flying saw saw lack of lubrication?
Why does the used roll forming machine flying saw saw lack of lubrication?
When the used roll forming machine produces steel pipes, the pipe fittings move at a constant speed according to the set speed, and the saw car is stationary relative to the unit before the sawing process. When the steel pipe reaches the set length, the clamping device of the saw car clamps the steel pipe, and the drive mechanism drives the saw car to move with the steel pipe and perform the sawing process until the sawing operation is completed. When the sawing process of the flying saw is completed, the driving device drives the saw carriage to return to the initial position. The reciprocating motion of the saw car is realized by the relative movement of the rack at the bottom of the saw car and the gear fixedly installed on the machine bed system.
Detail
When the used roll forming machine produces steel pipes, the pipe fittings move at a constant speed according to the set speed, and the saw car is stationary relative to the unit before the sawing process. When the steel pipe reaches the set length, the clamping device of the saw car clamps the steel pipe, and the drive mechanism drives the saw car to move with the steel pipe and perform the sawing process until the sawing operation is completed. When the sawing process of the flying saw is completed, the driving device drives the saw carriage to return to the initial position. The reciprocating motion of the saw car is realized by the relative movement of the rack at the bottom of the saw car and the gear fixedly installed on the machine bed system.
Weld quality failure caused by used welded pipe machines (9)
Weld quality failure caused by used welded pipe machines (9)
When manufacturing welded pipes for used welded pipe machines, judging that the quality of the welded pipes meets the standard depends on the quality of the welds. Therefore, the quality of the weld is very important, so sometimes it is necessary to rule out the quality of the weld. We perform analyses to understand weld quality failures.
Detail
When manufacturing welded pipes for used welded pipe machines, judging that the quality of the welded pipes meets the standard depends on the quality of the welds. Therefore, the quality of the weld is very important, so sometimes it is necessary to rule out the quality of the weld. We perform analyses to understand weld quality failures.
Contact information
Tel: +86-13392281699
Wechat: 13392281699
Email: zty@usedpipemill.com
Company address:No. A99, East Lecong Avenue, Lecong Town, Foshan City, Guangdong Province

Recommendation

Online Inquiry

留言应用名称:
底部留言
描述:

LINK

Contact Us

Tel (wechat): 13336487288
Wechat:+86 13336487288

WhatsApp:+86 13336487288
Email: zty@usedpipemill.com

Address: No. A99, Lecong Avenue East, Lecong Town, Foshan City, Guangdong Province

QRCODE

Copyright 0 2021 jinyujie. 粤ICP备13051810号 Powerby:  300.cn